Abstract The δ is an important stable phase that replaces the metastable γ'' in the microstructure of Inconel 625 superalloy. The present work aims to investigate the kinetic of δ-phase precipitation in the microstructure of Inconel 625 nickel-based superalloy aged at 550, 625 and 725 °C up to 1000 h. Aging temperatures were chosen based on the thermodynamic simulation using JMatPro software which indicated that this phase is stable at temperatures below 905 °C. Microstructure of the heat-treated samples was analyzed via SEM/EDS and microhardness evolution was performed by Vickers microhardness tests. The results have shown that the samples aged at 550 °C (all times), 625 °C (all times) and 725 °C up to 200 h did not presented microstructural evidences of δ precipitation. However, samples aged at 725 °C for 500 and 1000 h clearly presented an acicular δ-phase precipitated mainly at the grain boundaries. It was noted changes in the microhardness at different aging time and temperatures probably due to the presence of γ'' and/or δ phases. The sample aged at 625 °C for 1000 h presented the highest microhardness value (333 ± 10 HV).

Metastable β-type Ti alloys with non-toxic addition elements such as Mo, Zr, Sn, Ta and Nb were developed as an alternative to the widely used Ti-6Al-4V alloy for biomedical applications. These alloys possess enhanced biocompatibility and reduced elastic modulus in comparison with Ti-6Al-4V. Moreover, for orthopedic implants, low Young's modulus is required in order to avoid the stress shielding phenomenon. This study analyzes the microstructure and mechanical properties of a new Ti-12Mo-8Nb alloy after hot swaging, annealing at 950 ºC for 1h and water quenching. The alloy was characterized by X-ray diffraction, optical microscopy and transmission electron microscopy. Tensile tests were performed at room temperature. Young's modulus and hardness values were also measured. The structural characterization reveals a metastable β structure containing only a small amount of α and ω phases. Exhibiting a lower Young's modulus than Ti-6Al-4V and other previously studied Ti-Mo-Nb alloys, the Ti-12Mo-8Nb alloy can be a promising alternative for orthopedic application.

Beta titanium alloys were developed for biomedical applications due to the combination of its mechanical properties including low elasticity modulus, high strength, fatigue resistance, good ductility and with excellent corrosion resistance. With this perspective a metastable beta titanium alloy Ti-12Mo-13Nb was developed with the replacement of both vanadium and aluminum from the traditional alloy Ti-6Al-4V. This paper presents the microstructure, mechanical properties of the Ti-12Mo-13Nb hot swaged and aged at 500 °C for 24 h under high vacuum and then water quenched. The alloy structure was characterized by X-ray diffraction and transmission electron microscopy. Tensile tests were carried out at room temperature. The results show a microstructure consisting of a fine dispersed α phase in a β matrix and good mechanical properties including low elastic modulus. The results indicate that Ti-12Mo-13Nb alloy can be a promising alternative for biomedical application.

A partial isothermal section (Ti-TiSi2-TiB2 region) of the ternary Ti-Si-B system at 1250 ° C was determined from heat-treated alloys prepared via arc melting. Microstructural characterization has been carried out through scanning electron microscopy (SEM), x-ray diffraction (xRD) and wavelength dispersive spectrometry (WDS). The results have shown the stability of the near stoichiometric Ti6Si2B phase and a negligible solubility of boron in the Ti-silicides as well as of Si in the Ti-borides. The following three-phase equilibria have been observed in the Ti- TiSi2-TiB2 region: Ti ss+TiB+Ti6Si2B, Ti ss+Ti6Si2B+Ti5Si3, Ti5Si3+Ti6Si2B+TiB, Ti5Si3+TiB+Ti3B4, Ti5Si3+Ti3B4+TiB2, Ti5Si3+TiB2+Ti5Si4, Ti5Si4+TiB2+TiSi and TiSi+TiB2+TiSi2.